6061 t6 aluminium vs 7075 aluminium
6061 t6 aluminium vs 7075
Aluminiumlegerings 6061-T6 en 7075 word wyd gebruik in ingenieurstoepassings, maar hulle het verskillende eienskappe en is geskik vir verskillende doeleindes. Hieronder is 'n gedetailleerde vergelyking van hierdie twee legerings in terme van hul meganiese eienskappe, fisiese eienskappe, en tipiese gebruike:
Vergelyking tussen 6061-T6 en 7075 Aluminium
| Eiendom | 6061-T6 aluminium | 7075 Aluminium |
|---|
| Samestelling | 0.8-1.2% Mg, 0.4-0.8% En, 0.15-0.4% Cu, 0.04-0.35% Kr | 5.1-6.1% Zn, 2.1-2.9% Mg, 1.2-2.0% Cu, 0.18-0.28% Kr |
| Trek sterkte | 310 MPa (45 ksi) | 572 MPa (83 ksi) |
| Lewer krag | 275 MPa (40 ksi) | 503 MPa (73 ksi) |
| Verlenging by Breek | 12% | 11% |
| Hardheid (Brinell) | 95 HB | 150 HB |
| Modulus van elastisiteit | 68.9 GPa (10,000 ksi) | 71.7 GPa (10,400 ksi) |
| Digtheid | 2.70 g/cm³ | 2.81 g/cm³ |
| Moegheid Krag | 96 MPa (14 ksi) | 159 MPa (23 ksi) |
| Termiese geleidingsvermoë | 167 W/m·K | 130 W/m·K |
| Korrosieweerstand | Uitstekend | Reg tot arm (sonder beskermende laag) |
| Sweisbaarheid | Uitstekend | Arm |
| Bewerkbaarheid | Goed | Reg tot Goed |
| Hitte behandeling | Hitte behandelbaar tot T6 toestand | Hitte behandelbaar tot T6 of T73 toestand |
Sleutelverskille in eienskappe
- Sterkte:
- 7075 Aluminium is baie sterker, met 'n treksterkte van 572 MPa in vergelyking met 310 MPa vir 6061-T 6. Dit maak 7075 aluminium ideaal vir hoë-spanning strukturele toepassings.
- Korrosieweerstand:
- 6061-T6 aluminium het uitstekende weerstand teen korrosie, veral teen atmosferiese en mariene toestande, terwyl 7075 Aluminium het redelike tot swak weerstand teen korrosie en benodig dikwels 'n beskermende laag of anodisering vir gebruik in korrosiewe omgewings.
- Sweisbaarheid:
- 6061-T6 aluminium is hoogs sweisbaar, making it suitable for structures requiring frequent welding. 7075 Aluminium is difficult to weld and can suffer from cracking and brittleness after welding.
- Bewerkbaarheid:
- 6061-T6 aluminium is known for its good machinability, which is better than that of 7075 Aluminium, although 7075 still offers acceptable machinability for most applications.
- Digtheid:
- 7075 Aluminium is slightly denser (2.81 g/cm³) than 6061-T6 aluminium (2.70 g/cm³), which can affect weight-sensitive applications.
- Termiese geleidingsvermoë:
- 6061-T6 aluminium has better thermal conductivity (167 W/m·K) compared to 7075 Aluminium (130 W/m·K), making it preferable for heat-exchange applications.
Comparison of Uses
| Application Area | 6061-T6 aluminium | 7075 Aluminium |
|---|
| Lugvaart | Aircraft fittings, brandstoftenks, and fuselage structures | High-stress structural parts like aircraft wings, fuselage frames, and landing gear |
| Motor | Chassis, wheel spacers, and engine components | Racing components like suspension parts, gears, and shafts |
| Marine | Boat hulls, maste, en mariene toebehore | Not typically used due to poor corrosion resistance |
| General Construction | Structural components, pype, en rame | Not common; only when high strength is needed |
| Sports Equipment | Fietsrame, kamptoerusting, en skubadenks | Hoëprestasie-fietskomponente, klimtoerusting |
| Elektronika | Verhittingsbakke en elektriese toebehore | Word nie tipies gebruik nie; 6061 word verkies vir termiese toepassings |
| Verbruikersgoedere | Leertjies, meubels, en huishoudelike items | Premium produkte waar hoë sterkte verlang word, soos robuuste buitelugtoerusting |
Opsomming
- 6061-T6 aluminium is meer veelsydig, makliker om mee te werk, en het uitstekende korrosiebestandheid, maak dit geskik vir 'n wye reeks toepassings, insluitend mariene, motor, konstruksie, en elektronika.
- 7075 Aluminium bied voortreflike krag, maak dit ideaal vir hoë-stres toepassings soos lugvaart en hoëprestasie sporttoerusting, maar dit het swakker sweisbaarheid en weerstand teen korrosie, die gebruik daarvan in sekere omgewings beperk.