1. સામગ્રીની રચના 1100 એલ્યુમિનિયમ કોઇલ મુખ્યત્વે એલ્યુમિનિયમ અને તાંબાના નાના ભાગથી બનેલું હોય છે, સિલિકોન, મેંગેનીઝ અને અન્ય તત્વો, જ્યારે 3003 એલ્યુમિનિયમ કોઇલ મુખ્યત્વે એલ્યુમિનિયમ અને તાંબા અને મેંગેનીઝનો એક નાનો ભાગ બનેલો છે.
| સામગ્રીની રચના | 1100 એલ્યુમિનિયમ કોઇલ | 3003 એલ્યુમિનિયમ કોઇલ |
|---|
| અલ | ≥99.0% | ≥96.0% |
| કુ | ≤0.05% | 0.05%-0.20% |
| Mn | — | 1.0%-1.5% |
| અને | ≤0.60% | — |
| ફે | ≤0.05% | ≤0.70% |
| Zn | — | ≤0.10% |
| ના | — | — |
| અન્ય | ≤0.05% | ≤0.15% |
2. Density The density of 3003 aluminum coil is slightly higher than that of 1100 એલ્યુમિનિયમ કોઇલ, 2.72g/cm³ and 2.70g/cm³ respectively.
3. Strength The strength of 3003 aluminum coils is higher than that of 1100 એલ્યુમિનિયમ કોઇલ, 140-180MPa and 110-130MPa respectively.
4. Corrosion resistance The corrosion resistance of 3003 aluminum coil is better than that of 1100 એલ્યુમિનિયમ કોઇલ, especially in humid environment, its corrosion resistance is more prominent.
5. Processing performance The processing performance of 1100 aluminum coil is better than that of 3003 એલ્યુમિનિયમ કોઇલ, especially in cold working. જોકે, the processing performance of 3003 aluminum coil is relatively poor, and it is easy to produce surface wrinkles.
6. Weldability The weldability of 3003 aluminum coil is better than that of 1100 એલ્યુમિનિયમ કોઇલ, which is suitable for welding process.
7. Heat treatment performance The heat treatment performance of 1100 aluminum coil is better than that of 3003 એલ્યુમિનિયમ કોઇલ, and the properties of the material can be changed by heating and cooling.
8. હલકો 1100 aluminum coil has a low density and can be used for lightweight design. It is suitable for some products that require weight, such as aircraft components and vehicles.
9. Application fields 1100 aluminum coils are mainly used in lighting, aluminum mirrors, radiators and other fields, જ્યારે 3003 aluminum coils are widely used in automobiles, એરોસ્પેસ, બાંધકામ, electronics and other fields.
10. The price varies depending on the material composition and processability.