6061-O aluminium ntawv VS 6061-T6 txhuas ntawv

Dab tsi yog qhov txawv ntawm 6061-O thiab 6061-T6 txhuas ntawv?

6061-O aluminum sheet and 6061-T6 aluminum sheet are two common specifications of aluminum sheets in the 6000 series 6061. Lawv muaj cov yam ntxwv zoo dua. Dab tsi yog qhov txawv ntawm 6061-O thiab 6061-T6 txhuas ntawv? Qhov sib txawv tseem ceeb ntawm 6061-O thiab 6061-T6 txhuas daim hlau yog lawv cov khoom siv kho tshuab, especially strength and hardness, which are affected by the tempering process.

6061-O aluminum plate:

Kub: O (annealed)

Mechanical behavior:
Tensile zog: Typically approximately 124 MPa (18 ksi ua)
Yield zog: Typically approximately 55 MPa (8 ksi ua)
Elongation: usually around 25%
Hardness: lower
Formability: Excellent formability due to its softness. It can be molded, khoov, and molded easily without cracking or weakening.

Typical uses:
Typically used in applications where high strength is not a critical requirement but formability and corrosion resistance are critical.
Ideal for applications requiring deep drawing or forming processes such as automotive parts, cans and kitchenware.

6061-T6 aluminum plate:

Condition: T6 (solution heat treatment and artificial aging)
Mechanical behavior:
Tensile zog: Typically approximately 310 MPa (45 ksi ua)
Yield zog: Typically approximately 275 MPa (40 ksi ua)
Elongation: usually around 12%
Hardness: Harder compared to 6061-O due to precipitation hardening process.
Formability: Although still formable, 6061-T6 is less ductile than 6061-O due to increased strength and hardness. It may require more force to bend or form.

Typical uses:
Structural applications requiring high strength and good corrosion resistance, such as aerospace components, bicycle frames and structural components in construction.
Machined components requiring high strength and excellent machining properties.

Comparison Table:

Khoom6061-O Aluminum Sheet6061-T6 Aluminum Sheet
Tensile zogTypically around 124 MPa (18 ksi ua)Typically around 310 MPa (45 ksi ua)
Yield zogTypically around 55 MPa (8 ksi ua)Typically around 275 MPa (40 ksi ua)
ElongationTypically around 25%Typically around 12%
HardnessRelatively lowHigher
FormabilityZoo heevFormable, but less malleable
Typical UsesDeep drawing, forming processesKev siv cov qauv, machined components