Gịnị bụ ihe dị iche n'etiti 6061-O na 6061-T6 aluminum mpempe akwụkwọ?

6061-O aluminum sheet and 6061-T6 aluminum sheet are two common specifications of aluminum sheets in the 6000 usoro 6061. Ha nwere njirimara ka mma. Gịnị bụ ihe dị iche n'etiti 6061-O na 6061-T6 aluminum Ibé akwụkwọ? Isi ihe dị iche n'etiti 6061-O na 6061-T6 aluminum plates bụ ihe eji arụ ọrụ ha, especially strength and hardness, which are affected by the tempering process.

6061-O aluminum plate:

Iwe: O (annealed)

Mechanical behavior:
Ike ọdụdọ: Typically approximately 124 MPa (18 ksi)
Mpụta Ike: Typically approximately 55 MPa (8 ksi)
Ogologo oge: usually around 25%
Isi ike: lower
Formability: Excellent formability due to its softness. It can be molded, bent, and molded easily without cracking or weakening.

Typical uses:
Typically used in applications where high strength is not a critical requirement but formability and corrosion resistance are critical.
Ideal for applications requiring deep drawing or forming processes such as automotive parts, cans and kitchenware.

6061-T6 aluminum plate:

Condition: T6 (solution heat treatment and artificial aging)
Mechanical behavior:
Ike ọdụdọ: Typically approximately 310 MPa (45 ksi)
Mpụta Ike: Typically approximately 275 MPa (40 ksi)
Ogologo oge: usually around 12%
Isi ike: Harder compared to 6061-O due to precipitation hardening process.
Formability: Although still formable, 6061-T6 is less ductile than 6061-O due to increased strength and hardness. It may require more force to bend or form.

Typical uses:
Structural applications requiring high strength and good corrosion resistance, such as aerospace components, bicycle frames and structural components in construction.
Machined components requiring high strength and excellent machining properties.

Comparison Table: