ការយល់ដឹងអំពី 2024 លោហធាតុអាលុយមីញ៉ូម
2024 បន្ទះអាលុយមីញ៉ូមគឺជាអាលុយមីញ៉ូមរឹងធម្មតានៅក្នុងប្រព័ន្ធអាលុយមីញ៉ូម-ទង់ដែង-ម៉ាញ៉េស្យូម.
2024 aluminum sheet alloyវាមានកម្លាំងខ្ពស់ និងដំណើរការកាត់ល្អ។, កម្លាំងល្អ និងធន់នឹងកំដៅ, ប៉ុន្តែភាពធន់នឹងការ corrosion ខ្សោយ.
វាត្រូវបានគេប្រើយ៉ាងទូលំទូលាយនៅក្នុងរចនាសម្ព័ន្ធយន្តហោះ (ស្បែក, គ្រោងឆ្អឹង, ធ្នឹមឆ្អឹងជំនី, ក្បាលធំ, ល។), rivets, សមាសធាតុមីស៊ីល, មជ្ឈមណ្ឌលកង់ឡានដឹកទំនិញ, propeller components and various other structural parts.
តើអ្វីជា 6061 aluminum plate alloy?
6061 លោហធាតុអាលុយមីញ៉ូម is a heat-treatable and strengthened alloy with good formability, ភាពអាចផ្សារបាន។, និងភាពធន់.
6061 aluminium sheet alloy
វាក៏មានកម្លាំងមធ្យម និងអាចរក្សាបាននូវកម្លាំងដ៏ល្អបន្ទាប់ពីការ annealing.
The main alloying elements of 6061 aluminum alloy are magnesium and silicon, and they form Mg2S phase.
If it contains a certain amount of manganese and chromium, it can neutralize the bad effects of iron; sometimes a small amount of copper or zinc is added to increase the strength of the alloy without significantly reducing its corrosion resistance;
2024 អាលុយមីញ៉ូមទល់នឹង 6061 composition difference
ទាំងពីរ 2024 អាលុយមីញ៉ូ alloy និង 6061 alloy are metals with high hardness and good corrosion resistance and pressure resistance. The reason is that the chemical elements contained in the two aluminum alloys are different.
អាលុយមីញ៉ូម 2024 belongs to the AI-Cu-Mg system, និងអាលុយមីញ៉ូម 6061 belongs to the AI-Mg-Si system.
| Comparison of chemical composition of aluminum alloy 2024 និង 6061 |
| យ៉ាន់ស្ព័រ | និង | ហ្វេ | គ | ម | Mg | Cr | Zn | នៃ | ផ្សេងៗ | អាល់ |
| 2024 អាលុយមីញ៉ូម | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.10 | 0.25 | 0.15 | 0.15 | នៅសល់ |
| 6061 អាលុយមីញ៉ូម | 0.4-0.8 | 0.7 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | នៅសល់ |
2024 អាលុយមីញ៉ូមទល់នឹង 6061 price difference
Due to the copper content in its composition, 2024 aluminum alloy is more difficult to make plate ingots during production, with a higher failure rate, which results in an increase in its production cost compared to 6061 លោហធាតុអាលុយមីញ៉ូម. 2024 លោហធាតុអាលុយមីញ៉ូម, especially 2024-T351 model, has a higher hardness, which makes it difficult to roll with ordinary hot rolling mills. Due to production costs and technical limitations, the supply of 2024 aluminum alloy is relatively small, which naturally leads to its higher price.
The price of 2024 aluminum alloy plate is generally about RMB 20 per kilogram higher than that of 6061 aluminum alloy plate, while the price of cutting processing is more than RMB 40 per kilogram.
Which is better between 2024 aluminum plate and 6061 បន្ទះអាលុយមីញ៉ូម?
ទាំងពីរ 2024 សន្លឹកអាលុយមីញ៉ូមនិង 6061 aluminum sheet have their own characteristics, and their characteristics vary depending on the application scenario.
2024 aluminum sheet is an aviation-grade aluminum alloy that is widely used in demanding industrial fields due to its excellent strength and hardness.
6061 aluminum sheet is a common aluminum alloy with good comprehensive properties and is suitable for a variety of machining and industrial applications.
The price of 2024 aluminum sheet is usually higher than that of 6061 aluminum sheet due to differences in its production cost and material properties.
If your application does not require extreme strength and hardness, 6061 aluminum sheet can meet the requirements and is more economical.
If your working environment requires the material to have higher strength and wear resistance, then 2024 aluminum sheet may be a better choice.
លោហធាតុអាលុយមីញ៉ូម 2024 និង 6061 product types
 |  |  |
| 2024 6061 សន្លឹកអាលុយមីញ៉ូម | 2024 6061 សន្លឹកអាលុយមីញ៉ូម | 2024 6061 ខ្សែអាលុយមីញ៉ូម |
2024 អាលុយមីញ៉ូមទល់នឹង 6061 លក្ខណៈសម្បត្តិមេកានិច
Comparison of mechanical properties of Aluminum alloy 2024 និង 6061.
| ទ្រព្យសម្បត្តិ | អាលុយមីញ៉ូម Alloy 2024 | អាលុយមីញ៉ូម Alloy 6061 |
|---|
| Main Alloying Element | ស្ពាន់ (គ) | Magnesium (Mg) and Silicon (និង) |
| កម្លាំងទិន្នផល (0.2% offset) | 290-330 MPa (42-48 ខេស៊ី) | 240-270 MPa (35-39 ខេស៊ី) |
| កម្លាំង Tensile ចុងក្រោយ | 400-470 MPa (58-68 ខេស៊ី) | 310-350 MPa (45-51 ខេស៊ី) |
| ការពន្លូតនៅពេលសម្រាក | 10-20% | 8-18% |
| រឹង (Brinell) | 120-150 HB | 95-110 HB |
| កម្លាំងអស់កម្លាំង | ~140 MPa (20 ខេស៊ី) | ~96 MPa (14 ខេស៊ី) |
| ម៉ូឌុលនៃការបត់បែន | ~72 GPa (10.5 Msi) | ~69 GPa (10 Msi) |
| ដង់ស៊ីតេ | 2.78 g/cm³ | 2.70 g/cm³ |
| ចរន្តកំដៅ | 121 W/m·K | 151-167 W/m·K |
| ចំណុចរលាយ | 502°C (936°F) | 582°C (1080°F) |
| ភាពធន់នឹងសំណឹក | Lower than 6061, prone to corrosion | High, ជាពិសេសនៅក្នុងបរិស្ថានសមុទ្រ |
| សមត្ថភាពម៉ាស៊ីន | Good but slightly more difficult than 6061 | ល្អឥតខ្ចោះ, better machinability than 2024 |
| ភាពអាចផ្សារបាន។ | ក្រីក្រ (due to cracking in the heat-affected zone) | ល្អឥតខ្ចោះ, widely used for welded structures |
| ទម្រង់បែបបទ | Fair, limited due to high strength | ល្អ, excellent for complex shapes and extrusions |
| កម្មវិធី | រចនាសម្ព័ន្ធយន្តហោះ, កម្មវិធីយោធា | Structural applications, marine frames, គ្រឿងបន្លាស់រថយន្ត |