6061 t6 aluminium vs 7075 aluminium
6061 t6 aluminium vs 7075
Aluminium admixtum 6061-T6 and 7075 late in ipsum applications, sed proprietates habent diversas, et ad diversos usus conveniunt. Infra est accurata comparatio harum duarum mixtionum secundum earum proprietates mechanicas, physica, ac typicam usus:
Comparatio inter 6061-T6 et 7075 aluminium
| Property | 6061-T6 Aluminum | 7075 aluminium |
|---|
| Compositio | 0.8-1.2% Mg, 0.4-0.8% And, 0.15-0.4% Cu, 0.04-0.35% Cr | 5.1-6.1% Zn, 2.1-2.9% Mg, 1.2-2.0% Cu, 0.18-0.28% Cr |
| distrahentes Fortitudo | 310 MPa (45 ksi) | 572 MPa (83 ksi) |
| cede virtus | 275 MPa (40 ksi) | 503 MPa (73 ksi) |
| Elongation at Break | 12% | 11% |
| duritia (Brinell) | 95 HB | 150 HB |
| Modulus Elasticitatis | 68.9 GPa (10,000 ksi) | 71.7 GPa (10,400 ksi) |
| Density | 2.70 g/cm³ | 2.81 g/cm³ |
| Lassitudo fortitudo | 96 MPa (14 ksi) | 159 MPa (23 ksi) |
| Scelerisque Conductivity | 167 W/m·K | 130 W/m·K |
| Corrosio Resistentia | Praeclarus | Pulchra ad pauperem (sine tutela coating) |
| Weldability | Praeclarus | Pauper |
| Machinability | bonum | Pulchra ad bonum |
| Calor Curatio | Ad T6 conditio æstus treatable | Aestus treatable to T6 or T73 condition |
Key Differentiae in Properties
- Fortitudo:
- 7075 aluminium multo fortior, cum distrahentes fortitudinem 572 MPa comparari 310 MPa for 6061-T6. Hoc facit 7075 aluminium specimen pro summus accentus structurarum applicationes.
- Corrosio Resistentia:
- 6061-T6 Aluminum habet optimum corrosione resistentia, praesertim contra conditiones atmosphaericas et marinas, dum 7075 aluminium aequum est ad pauperem corrosio resistentia et saepe requirit tutela membrana vel anodizing usui in ambitus mordax.
- Weldability:
- 6061-T6 Aluminum valde weldable, idoneos faciendos ad structuras poscentes crebra glutino. 7075 aluminium difficile pactionem et potest laborare crepuit et fragilitas post glutino.
- Machinability:
- 6061-T6 Aluminum notum est pro suo bono machinability, quod melius est quam 7075 aluminium, quamvis 7075 tamen offert gratum machinability ad omnium applicationum.
- Density:
- 7075 aluminium leviter densior (2.81 g/cm³) quam 6061-T6 Aluminum (2.70 g/cm³), quae afficit pondus-sensitivum applicationes.
- Scelerisque Conductivity:
- 6061-T6 Aluminum scelerisque conductivity melius est (167 W/m·K) comparari 7075 aluminium (130 W/m·K), ut potior sit calor commutationem applications.
Comparatio Usus
| Applicationem Area | 6061-T6 Aluminum | 7075 aluminium |
|---|
| Aerospace | Aircrafts caerimonias, cibus obterere, et fuselage structurae | Princeps accentus structurarum partes sicut elit alas, fuselage tabulae, et portum calces |
| Automotive | Chassis, rota spacers, et engine components | Racing components sicut suspensionis partes, anni, et spicula |
| Marine | Phasellus carinae, malos, et marinis caerimonias | Non typice usus est propter pauperem corrosio resistentia |
| Constructio Generalis | Structural components, limbis, et tabulae | Non commune; nisi cum magno robore opus est |
| Ludis Equipment | Bicycle tabulae, castra apparatu, Aliquam ac lacus | Summus perficientur components vehentem, apparatu scandere |
| Electronics | Calor desidit et electricum caerimonias | Non typice usus est; 6061 scelerisque applications est malle |
| Consumer bonis | scalae, supellex, et supellectile | Magnum products ubi princeps viribus desideratur, ut praeruptam velit calces |
Summarium
- 6061-T6 Aluminum est mobilior, facilius ad opus, et habet optimam corrosionem resistentiam, idoneus ut amplis applicationibus, comprehendo marine, automotive, constructione, et electronics.
- 7075 aluminium superior viribus, summus accentus applications faciens illud bonum sicut aerospace et ludis apparatu summus perficientur, sed deteriorem indubilitatem et corrosionem habet resistentiam, limitandi usum in quibusdam ambitibus.