Aluminum alloys 6061-T6 and 7075 are widely used in engineering applications, but they have different properties and are suited to different purposes. Below is a detailed comparison of these two alloys in terms of their mechanical properties, physical properties, and typical uses:
Comparison Between 6061-T6 and 7075 Aliuminis
| Turtas | 6061-T6 aliuminis | 7075 Aliuminis |
|---|
| Composition | 0.8-1.2% Mg, 0.4-0.8% Ir, 0.15-0.4% Cu, 0.04-0.35% Kr | 5.1-6.1% Zn, 2.1-2.9% Mg, 1.2-2.0% Cu, 0.18-0.28% Kr |
| Tempimo stiprumas | 310 MPa (45 ksi) | 572 MPa (83 ksi) |
| Derlingumo stiprumas | 275 MPa (40 ksi) | 503 MPa (73 ksi) |
| Pailgėjimas lūžio metu | 12% | 11% |
| Kietumas (Brinelis) | 95 HB | 150 HB |
| Elastingumo modulis | 68.9 GPa (10,000 ksi) | 71.7 GPa (10,400 ksi) |
| Tankis | 2.70 g/cm³ | 2.81 g/cm³ |
| Fatigue Strength | 96 MPa (14 ksi) | 159 MPa (23 ksi) |
| Thermal Conductivity | 167 W/m·K | 130 W/m·K |
| Atsparumas korozijai | Puikiai | Fair to Poor (without protective coating) |
| Suvirinamumas | Puikiai | Poor |
| Apdirbamumas | Gerai | Fair to Good |
| Terminis apdorojimas | Heat treatable to T6 condition | Heat treatable to T6 or T73 condition |
Key Differences in Properties
- Strength:
- 7075 Aliuminis is much stronger, with a tensile strength of 572 MPa compared to 310 MPa for 6061-T6. This makes 7075 aluminum ideal for high-stress structural applications.
- Atsparumas korozijai:
- 6061-T6 aliuminis turi puikų atsparumą korozijai, especially against atmospheric and marine conditions, while 7075 Aliuminis has fair to poor corrosion resistance and often requires a protective coating or anodizing for use in corrosive environments.
- Suvirinamumas:
- 6061-T6 aliuminis is highly weldable, making it suitable for structures requiring frequent welding. 7075 Aliuminis is difficult to weld and can suffer from cracking and brittleness after welding.
- Apdirbamumas:
- 6061-T6 aliuminis is known for its good machinability, which is better than that of 7075 Aliuminis, although 7075 still offers acceptable machinability for most applications.
- Tankis:
- 7075 Aliuminis is slightly denser (2.81 g/cm³) than 6061-T6 aliuminis (2.70 g/cm³), which can affect weight-sensitive applications.
- Thermal Conductivity:
- 6061-T6 aliuminis has better thermal conductivity (167 W/m·K) compared to 7075 Aliuminis (130 W/m·K), making it preferable for heat-exchange applications.
Comparison of Uses
| Application Area | 6061-T6 aliuminis | 7075 Aliuminis |
|---|
| Aerospace | Aircraft fittings, fuel tanks, and fuselage structures | High-stress structural parts like aircraft wings, fuselage frames, and landing gear |
| Automotive | Chassis, wheel spacers, and engine components | Racing components like suspension parts, gears, and shafts |
| Marine | Boat hulls, masts, and marine fittings | Not typically used due to poor corrosion resistance |
| General Construction | Structural components, piping, ir rėmeliai | Not common; only when high strength is needed |
| Sports Equipment | Dviračių rėmai, camping equipment, and scuba tanks | High-performance bicycle components, climbing equipment |
| Electronics | Heat sinks and electrical fittings | Not typically used; 6061 is preferred for thermal applications |
| Consumer Goods | Ladders, furniture, and household items | Premium products where high strength is desired, such as rugged outdoor gear |
Summary
- 6061-T6 aliuminis is more versatile, easier to work with, and has excellent corrosion resistance, making it suitable for a wide range of applications, including marine, automobilių, construction, ir elektronika.
- 7075 Aliuminis offers superior strength, making it ideal for high-stress applications like aerospace and high-performance sports equipment, but it has poorer weldability and corrosion resistance, limiting its use in certain environments.