What is the difference between 6061-O and 6061-T6 aluminum sheet?
6061-O aluminum sheet and 6061-T6 aluminum sheet are two common specifications of aluminum sheets in the 6000 цуврал 6061. They have better characteristics. What is the difference between 6061-O and 6061-T6 aluminum sheets? The main difference between 6061-O and 6061-T6 aluminum plates is their mechanical properties, especially strength and hardness, which are affected by the tempering process.
6061-O aluminum plate:
Ааш зан: О (annealed)
Mechanical behavior:
Суналтын бат бэх: Typically approximately 124 МПа (18 ksi)
Ургацын хүч: Typically approximately 55 МПа (8 ksi)
Elongation: usually around 25%
Хатуу байдал: lower
Formability: Excellent formability due to its softness. It can be molded, bent, and molded easily without cracking or weakening.
Typical uses:
Typically used in applications where high strength is not a critical requirement but formability and corrosion resistance are critical.
Ideal for applications requiring deep drawing or forming processes such as automotive parts, cans and kitchenware.
6061-T6 aluminum plate:
Condition: T6 (solution heat treatment and artificial aging)
Mechanical behavior:
Суналтын бат бэх: Typically approximately 310 МПа (45 ksi)
Ургацын хүч: Typically approximately 275 МПа (40 ksi)
Elongation: usually around 12%
Хатуу байдал: Harder compared to 6061-O due to precipitation hardening process.
Formability: Although still formable, 6061-T6 is less ductile than 6061-O due to increased strength and hardness. It may require more force to bend or form.
Typical uses:
Structural applications requiring high strength and good corrosion resistance, such as aerospace components, bicycle frames and structural components in construction.
Machined components requiring high strength and excellent machining properties.
Comparison Table:
Өмч | 6061-O Aluminum Sheet | 6061-T6 Aluminum Sheet |
---|
Суналтын бат бэх | Typically around 124 МПа (18 ksi) | Typically around 310 МПа (45 ksi) |
Ургацын хүч | Typically around 55 МПа (8 ksi) | Typically around 275 МПа (40 ksi) |
Elongation | Typically around 25% | Typically around 12% |
Хатуу байдал | Relatively low | Higher |
Formability | Маш сайн | Formable, but less malleable |
Typical Uses | Deep drawing, forming processes | Structural applications, machined components |