Aluminij 6065 VS 6005 Aluminij

Differences Between Aluminum 6065 And 6005–Aluminij 6065 Vs 6005

6000 series aluminum 6005 in 6065

Both aluminum alloy 6005 and aluminum alloy 6065 are less common alloys in the 6000 serije. The 6 series aluminum metal has added elements such as silicon and magnesium, and has higher strength and corrosion resistance than the 1000 series pure aluminum alloy. Among them, aluminij 6065 in 6005 are rare aluminum metals in the 6xxx series, and there are similar characteristics and differences between the two.

Kaj je 6065 aluminijeve zlitine?

6065 aluminum alloy is a high-strength aluminum alloy, mainly composed of aluminum, magnesium and silicon.

6065 aluminum has high strength, and the service strength is usually between 300 MPa and 400 MPa, and the tensile strength is between 350MPa and 450 MPa.

6065 aluminum alloy is an aluminum alloy material with excellent performance and wide application.

6065 aluminum alloy can obtain good casting performance or processing plasticity, which is easy to make products of various shapes and specifications.

Zato, it has strong applicability in many fields such as aerospace, shipbuilding, prevoz, architectural decoration, electronic appliances, itd.

6065 aluminum alloy can increase its strength through heat treatment. Common heat treatment methods include aging treatment (6065 T6) and natural aging treatment (6065 T4).

Introduction to 6005 aluminijeve zlitine

Kaj je 6005 aluminij? 6005 aluminum alloy is a medium-strength and high-corrosion-resistant aluminum alloy belonging to the Al-Mg-Si series.

Aluminum alloy 6005 has good processing performance, welding performance and forming performance, and can be widely used in many fields.

6005 aluminum alloy has excellent welding performance and can be connected by a variety of welding methods, such as argon arc welding, resistance welding, laser welding, itd.

This also makes 6005 aluminum alloy easier to process and can be formed by cutting, drilling, milling, stamping and other methods.

6005 aluminum alloy has good corrosion resistance and has good stability to most common corrosive media such as air, water, acid, itd.

It can be well applied in outdoor and humid environments.

6005 aluminum alloy is closely related to 6005A aluminijeve zlitine, but it is not exactly the same.

The main difference between the two alloys is that the minimum percentage of aluminum in 6005 is higher than that in 6005A (but the maximum percentage is basically the same).

What is the difference between 6065 aluminum and 6005 aluminij?

Aluminij 6065 vs 6005 chemical composition

Metal element composition table (%)
Element	Al	Cr	Cu	Fe	Mg	Mn	Si	Ti	Zn
6005	97.5-99	≤0.1	≤0.1	≤0.35	0.4-0.6	≤0.1	0.6-0.9	≤0.1	≤0.1
6065	97.5-99.5	≤0.1	≤0.1	≤0.35	0.05	0.05	0.3	≤0.1	0.05

Aluminij 6065 vs 6005 density difference

Density of aluminum	aluminum density in lb/in³	density of aluminum kg/m³
6005	0.097	2700
6065	0.098	2720

Aluminij 6065 vs 6005 mechanical properties comparison

Mechanical Properties Comparison of 6065 vs. 6005 Aluminij
Property	6065-T6 Aluminum	6005-T6 Aluminum
Tensile Strength	265 MPa (38.4 ksi)	295 MPa (42.8 ksi)
Yield Strength	225 MPa (32.6 ksi)	255 MPa (37 ksi)
Elongation at Break	10%	12%
Hardness (Brinell)	95 HB	93 HB

The difference between aluminum 6065 in 6005 in usage

Property	6005 Aluminij	6065 Aluminij
General Use	Structural applications where moderate strength is needed	Applications requiring a balance of strength, odpornost proti koroziji, and appearance
Structural Components	Extrusions for bridges, towers, railings, and frames	Architectural applications, including window frames and door frames
Transportation	Truck bodies, marine components, and railway car components	Bicycle frames, automotive parts, and recreational equipment
Machinability	Moderate; suitable for profiles requiring medium complexity	Good; often chosen when a combination of machinability and moderate strength is needed
Corrosion Resistance	Good; suitable for outdoor and marine environments	Excellent; ideal for outdoor applications needing long-term durability
Heat Treatment	Often supplied in T5 or T6 temper for enhanced strength	Often supplied in T6 temper for optimal strength and appearance
Weldability	Good, but may require post-weld heat treatment for optimal properties	Good; well-suited for welding, especially in thinner sections
Appearance	Not typically chosen for high-appearance applications	Preferred when aesthetics and surface finish are important
Common Applications	Furniture, ladders, and other structural applications	Sporting goods, bicycle frames, decorative trims, and automotive accessories