1. Përbërja e materialit 1100 spiralja e aluminit përbëhet kryesisht nga alumini dhe një pjesë e vogël prej bakri, silikon, mangani dhe elementë të tjerë, ndërsa 3003 spiralja e aluminit përbëhet kryesisht nga alumini dhe një pjesë e vogël e bakrit dhe manganit.
| Përbërja e materialit | 1100 spirale alumini | 3003 spirale alumini |
|---|
| Al | ≥99.0% | ≥96.0% |
| Cu | ≤0.05% | 0.05%-0.20% |
| Mn | — | 1.0%-1.5% |
| Dhe | ≤0.60% | — |
| Fe | ≤0.05% | ≤0.70% |
| Zn | — | ≤0.10% |
| Nga | — | — |
| Të tjerët | ≤0.05% | ≤0.15% |
2. Density The density of 3003 aluminum coil is slightly higher than that of 1100 spirale alumini, 2.72g/cm³ and 2.70g/cm³ respectively.
3. Strength The strength of 3003 aluminum coils is higher than that of 1100 aluminum coils, 140-180MPa and 110-130MPa respectively.
4. Corrosion resistance The corrosion resistance of 3003 aluminum coil is better than that of 1100 spirale alumini, especially in humid environment, its corrosion resistance is more prominent.
5. Processing performance The processing performance of 1100 aluminum coil is better than that of 3003 spirale alumini, especially in cold working. Megjithatë, the processing performance of 3003 aluminum coil is relatively poor, and it is easy to produce surface wrinkles.
6. Weldability The weldability of 3003 aluminum coil is better than that of 1100 spirale alumini, which is suitable for welding process.
7. Heat treatment performance The heat treatment performance of 1100 aluminum coil is better than that of 3003 spirale alumini, and the properties of the material can be changed by heating and cooling.
8. Të lehta 1100 aluminum coil has a low density and can be used for lightweight design. It is suitable for some products that require weight, such as aircraft components and vehicles.
9. Application fields 1100 aluminum coils are mainly used in lighting, aluminum mirrors, radiators and other fields, ndërsa 3003 aluminum coils are widely used in automobiles, aerospace, ndërtimi, electronics and other fields.
10. The price varies depending on the material composition and processability.