Differences Between Aluminum 6065 And 6005–Алюминий 6065 Vs 6005
6000 series aluminum 6005 ва 6065
Both aluminum alloy 6005 and aluminum alloy 6065 are less common alloys in the 6000 силсила. Дар 6 series aluminum metal has added elements such as silicon and magnesium, and has higher strength and corrosion resistance than the 1000 series pure aluminum alloy. Дар байни онҳо, алюминий 6065 ва 6005 are rare aluminum metals in the 6xxx series, and there are similar characteristics and differences between the two.
Чӣ аст 6065 aluminum alloy?
6065 aluminum alloy is a high-strength aluminum alloy, mainly composed of aluminum, magnesium and silicon.
6065 aluminum has high strength, and the service strength is usually between 300 MPa and 400 МПа, and the tensile strength is between 350MPa and 450 МПа.
6065 aluminum alloy is an aluminum alloy material with excellent performance and wide application.
6065 aluminum alloy can obtain good casting performance or processing plasticity, which is easy to make products of various shapes and specifications.
Бинобар ин, it has strong applicability in many fields such as aerospace, shipbuilding, нақлиёт, architectural decoration, electronic appliances, ва ғайра.
6065 aluminum alloy can increase its strength through heat treatment. Common heat treatment methods include aging treatment (6065 T6) and natural aging treatment (6065 T4).
Introduction to 6005 aluminum alloy
Чӣ аст 6005 алюминий? 6005 aluminum alloy is a medium-strength and high-corrosion-resistant aluminum alloy belonging to the Al-Mg-Si series.
Хӯлаи алюминий 6005 has good processing performance, welding performance and forming performance, and can be widely used in many fields.
6005 aluminum alloy has excellent welding performance and can be connected by a variety of welding methods, such as argon arc welding, resistance welding, laser welding, ва ғайра.
This also makes 6005 aluminum alloy easier to process and can be formed by cutting, drilling, milling, stamping and other methods.
6005 aluminum alloy has good corrosion resistance and has good stability to most common corrosive media such as air, water, acid, ва ғайра.
It can be well applied in outdoor and humid environments.
6005 aluminum alloy is closely related to 6005A aluminum alloy, but it is not exactly the same.
The main difference between the two alloys is that the minimum percentage of aluminum in 6005 is higher than that in 6005A (but the maximum percentage is basically the same).
What is the difference between 6065 aluminum and 6005 алюминий?
Алюминий 6065 vs 6005 chemical composition
Metal element composition table (%) |
Element | Ал | Cr | Cu | Фе | Mg | Мн | Ва | Аз | Зн |
6005 | 97.5-99 | ≤0.1 | ≤0.1 | ≤0.35 | 0.4-0.6 | ≤0.1 | 0.6-0.9 | ≤0.1 | ≤0.1 |
6065 | 97.5-99.5 | ≤0.1 | ≤0.1 | ≤0.35 | 0.05 | 0.05 | 0.3 | ≤0.1 | 0.05 |
Алюминий 6065 vs 6005 density difference
Density of aluminum | aluminum density in lb/in³ | density of aluminum kg/m³ |
6005 | 0.097 | 2700 |
6065 | 0.098 | 2720 |
Алюминий 6065 vs 6005 mechanical properties comparison
Mechanical Properties Comparison of 6065 vs. 6005 Алюминий |
Амвол | 6065-T6 Алюминий | 6005-T6 Алюминий |
Устувории кашишӣ | 265 МПа (38.4 кси) | 295 МПа (42.8 кси) |
Қувваи ҳосилнокӣ | 225 МПа (32.6 кси) | 255 МПа (37 кси) |
Дарозии танаффус | 10% | 12% |
Сахтӣ (Бринелл) | 95 HB | 93 HB |
The difference between aluminum 6065 ва 6005 in usage
Амвол | 6005 Алюминий | 6065 Алюминий |
---|
General Use | Structural applications where moderate strength is needed | Applications requiring a balance of strength, муқовимат ба зангзании, and appearance |
Structural Components | Extrusions for bridges, towers, railings, ва чорчубахо | Architectural applications, including window frames and door frames |
Transportation | Truck bodies, marine components, and railway car components | Чорчубахои велосипед, automotive parts, and recreational equipment |
Қобилияти коркард | Moderate; suitable for profiles requiring medium complexity | Хуб; often chosen when a combination of machinability and moderate strength is needed |
Муқовимат ба зангзанӣ | Хуб; suitable for outdoor and marine environments | Аъло; ideal for outdoor applications needing long-term durability |
Табобати гармӣ | Often supplied in T5 or T6 temper for enhanced strength | Often supplied in T6 temper for optimal strength and appearance |
Кафшерпазирӣ | Хуб, but may require post-weld heat treatment for optimal properties | Хуб; well-suited for welding, especially in thinner sections |
Appearance | Not typically chosen for high-appearance applications | Preferred when aesthetics and surface finish are important |
Common Applications | Furniture, ladders, and other structural applications | Sporting goods, bicycle frames, decorative trims, and automotive accessories |
Learn More:5052 vs 6061