Differences Between Aluminum 6065 And 6005–I-Aluminium 6065 Vs 6005
6000 series aluminum 6005 futhi 6065
Both aluminum alloy 6005 and aluminum alloy 6065 are less common alloys in the 6000 uchungechunge. I 6 series aluminum metal has added elements such as silicon and magnesium, and has higher strength and corrosion resistance than the 1000 series pure aluminum alloy. Phakathi kwazo, i-aluminium 6065 futhi 6005 are rare aluminum metals in the 6xxx series, and there are similar characteristics and differences between the two.
Yini 6065 ingxube ye-aluminium?
6065 aluminum alloy is a high-strength aluminum alloy, mainly composed of aluminum, magnesium and silicon.
6065 aluminum has high strength, and the service strength is usually between 300 MPa and 400 I-MPa, and the tensile strength is between 350MPa and 450 I-MPa.
6065 aluminum alloy is an aluminum alloy material with excellent performance and wide application.
6065 aluminum alloy can obtain good casting performance or processing plasticity, which is easy to make products of various shapes and specifications.
Ngakho-ke, it has strong applicability in many fields such as aerospace, shipbuilding, ezokuthutha, architectural decoration, electronic appliances, njll.
6065 aluminum alloy can increase its strength through heat treatment. Common heat treatment methods include aging treatment (6065 T6) and natural aging treatment (6065 T4).
Introduction to 6005 ingxube ye-aluminium
Yini 6005 i-aluminium? 6005 aluminum alloy is a medium-strength and high-corrosion-resistant aluminum alloy belonging to the Al-Mg-Si series.
Ingxube ye-aluminium 6005 has good processing performance, welding performance and forming performance, futhi ingasetshenziswa kabanzi emikhakheni eminingi.
6005 aluminum alloy has excellent welding performance and can be connected by a variety of welding methods, such as argon arc welding, resistance welding, laser welding, njll.
This also makes 6005 aluminum alloy easier to process and can be formed by cutting, drilling, milling, stamping and other methods.
6005 aluminum alloy has good corrosion resistance and has good stability to most common corrosive media such as air, water, acid, njll.
It can be well applied in outdoor and humid environments.
6005 aluminum alloy is closely related to 6005A ingxube ye-aluminium, but it is not exactly the same.
The main difference between the two alloys is that the minimum percentage of aluminum in 6005 is higher than that in 6005A (but the maximum percentage is basically the same).
What is the difference between 6065 aluminum and 6005 i-aluminium?
I-Aluminium 6065 vs 6005 ukwakheka kwamakhemikhali
Metal element composition table (%) |
Isici | Al | Cr | Cu | Fe | Mg | UMn | Futhi | Kwe | Zn |
6005 | 97.5-99 | ≤0.1 | ≤0.1 | ≤0.35 | 0.4-0.6 | ≤0.1 | 0.6-0.9 | ≤0.1 | ≤0.1 |
6065 | 97.5-99.5 | ≤0.1 | ≤0.1 | ≤0.35 | 0.05 | 0.05 | 0.3 | ≤0.1 | 0.05 |
I-Aluminium 6065 vs 6005 density difference
Density of aluminum | aluminum density in lb/in³ | density of aluminum kg/m³ |
6005 | 0.097 | 2700 |
6065 | 0.098 | 2720 |
I-Aluminium 6065 vs 6005 mechanical properties comparison
Mechanical Properties Comparison of 6065 vs. 6005 I-Aluminium |
Impahla | 6065-T6 Aluminium | 6005-T6 Aluminium |
Amandla Okuqina | 265 I-MPa (38.4 ksi) | 295 I-MPa (42.8 ksi) |
Isivuno Amandla | 225 I-MPa (32.6 ksi) | 255 I-MPa (37 ksi) |
Elongation at Break | 10% | 12% |
Ukuqina (Brinell) | 95 HB | 93 HB |
The difference between aluminum 6065 futhi 6005 in usage
Impahla | 6005 I-Aluminium | 6065 I-Aluminium |
---|
General Use | Structural applications where moderate strength is needed | Applications requiring a balance of strength, ukumelana nokugqwala, and appearance |
Structural Components | Extrusions for bridges, towers, izinsimbi, kanye namafreyimu | Architectural applications, including window frames and door frames |
Transportation | Truck bodies, marine components, and railway car components | Amafreyimu ebhayisikili, izingxenye zezimoto, and recreational equipment |
Ukusebenziseka kalula | Moderate; suitable for profiles requiring medium complexity | Kuhle; often chosen when a combination of machinability and moderate strength is needed |
Ukumelana Nokugqwala | Kuhle; suitable for outdoor and marine environments | Kuhle kakhulu; ideal for outdoor applications needing long-term durability |
Ukwelashwa Kokushisa | Often supplied in T5 or T6 temper for enhanced strength | Often supplied in T6 temper for optimal strength and appearance |
Ukushisela | Kuhle, but may require post-weld heat treatment for optimal properties | Kuhle; well-suited for welding, especially in thinner sections |
Appearance | Not typically chosen for high-appearance applications | Preferred when aesthetics and surface finish are important |
Common Applications | Furniture, izitebhisi, and other structural applications | Sporting goods, bicycle frames, decorative trims, and automotive accessories |
Learn More:5052 vs 6061